| 材料 | ||||||
工作温度a | WCBb | 304 | 316 | ICr5Mo | 15CrMoc | 12Cr2MoI | 304L、CF3 |
℃ | CF8 | CF8M | CD5 | WC6 | WC9 | 316L、CF3M | |
| 最高允许工作压力 Mpa | ||||||
(-29~38) | 25.55 | 24.83 | 24.83 | 25.86 | 25.86 | 25.86 | 20.69 |
93.5 | 23.28 | 20.69 | 21.34 | 25.69 | 25.86 | 25.86 | 17.45 |
149 | 22.62 | 18.62 | 19.28 | 24.69 | 24.90 | 25.10 | 15.66 |
204.5 | 21.86 | 17.14 | 17.72 | 24.34 | 23.90 | 24.34 | 14.24 |
260 | 20.66 | 16.07 | 16.48 | 22.93 | 22.93 | 22.93 | 13.17 |
315.5 | 18.86 | 15.07 | 15.55 | 20.86 | 20.86 | 20.86 | 12.41 |
343.5 | 18.52 | 14.83 | 15.31 | 20.28 | 20.28 | 20.28 | 12.07 |
371 | 18.38 | 14.66 | 14.97 | 19.59 | 19.59 | 19.59 | 11.83 |
399 | 17.38 | 14.31 | 14.72 | 18.21 | 18.34 | 18.34 | 11.59 |
426.5 | 14.21 | 13.90 | 14.55 | 17.52 | 17.52 | 17.52 | 11.34 |
454.5 | 9.24 | 13.66 | 14.41 | 16.66 | 16.79 | 16.79 | 11.10 |
482 | 5.93 | 13.41 | 14.31 | 12.76 | 15.48 | 15.48 | — |
510 | 3.55 | 13.17 | 13.31 | 9.45 | 11.00 | 13.00 | — |
538 | 1.79 | 11.07 | 12.07 | 6.86 | 7.45 | 9.00 | — |
565.5 | — | 10.66 | 11.86 | 4.97 | 4.97 | 6.03 | — |
593.5 | — | 8.86 | 10.52 | 3.41 | 3.31 | 3.79 | — |
621 | — | 6.86 | 8.17 | 2.14 | 2.14 | 2.38 | — |
649 | — | 5.31 | 6.38 | 1.17 | 1.31 | 1.41 | — |
676.5 | — | 3.90 | 5.07 | — | — | — | — |
704.5 | — | 2.97 | 4.03 | — | — | — | — |
732.0 | — | 2.14 | 3.31 | — | — | — | — |
760.0 | — | 1.66 | 2.62 | — | — | — | — |
788.0 | — | 1.17 | 2 | — | — | — | — |
815.5 | — | 0.93 | 1.41 | — | — | — | — |
a 对于表中列出的允许在低温下工作的材料,在低于-29℃的任何温度下工作的压力额定值不得大于 | |||||||
表中列出的-29~38℃的额定值。 | |||||||
b 允许但不推荐在高于425℃时长期使用:含碳量要求w(C)<0.24%。 | |||||||
c 允许但不推荐在高于595℃时长期使用。 |