公称 | 钢号 |
| 强度试 | |||||||||||||||
压力 | 200 | 250 | 300 | 350 | 400 | 425 | 450 | 475 | 500 | 510 | 520 | 530 | 540 | 550 | 560 | 570 | 压验力 | |
Mpa |
| Mpa | ||||||||||||||||
1.0 | 20 | 0.98 | 0.88 | 0.78 | 0.69 | 0.63 | 0.55 | 0.42 |
|
|
|
|
|
|
|
|
| 1.5 |
25 | 0.98 | 0.88 | 0.78 | 0.69 | 0.63 | 0.55 | 0.42 |
|
|
|
|
|
|
|
|
| ||
ZG200-400 | 0.98 | 0.88 | 0.78 | 0.69 | 0.63 | 0.55 | 0.42 |
|
|
|
|
|
|
|
|
| ||
ZG230-450 | 0.98 | 0.88 | 0.78 | 0.69 | 0.63 | 0.55 | 0.42 |
|
|
|
|
|
|
|
|
| ||
15CrMo | 0.98 | 0.94 | 0.90 | 0.86 | 0.82 | 0.80 | 0.78 | 0.72 | 0.63 | 0.55 | 0.47 | 0.42 | 0.37 | 0.33 |
|
| ||
ZG20CrMo | 0.98 | 0.94 | 0.90 | 0.86 | 0.82 | 0.80 | 0.78 | 0.72 | 0.63 | 0.55 |
|
|
|
|
|
| ||
12CrlMoV | 0.98 | 0.94 | 0.90 | 0.86 | 0.82 | 0.80 | 0.78 | 0.74 | 0.70 | 0.69 | 0.63 | 0.55 | 0.49 | 0.44 | 0.39 | 0.35 | ||
15CrlMolV | 0.98 | 0.94 | 0.90 | 0.86 | 0.82 | 0.80 | 0.78 | 0.74 | 0.70 | 0.69 | 0.63 | 0.55 | 0.49 | 0.44 | 0.39 | 0.35 | ||
ZG20CrMoV | 0.98 | 0.94 | 0.90 | 0.86 | 0.82 | 0.80 | 0.78 | 0.74 | 0.70 | 0.69 | 0.63 | 0.55 | 0.49 |
|
|
| ||
ZG15CrlMolV | 0.98 | 0.94 | 0.90 | 0.86 | 0.82 | 0.80 | 0.78 | 0.74 | 0.70 | 0.69 | 0.63 | 0.55 | 0.49 | 0.44 | 0.39 | 0.35 | ||
1Cr5Mo | 0.98 | 0.94 | 0.90 | 0.84 | 0.76 | 0.70 | 0.63 | 0.54 | 0.44 | 0.39 | 0.35 | 0.31 | 0.27 | 0.25 |
|
| ||
ZG1Cr5Mo | 0.98 | 0.94 | 0.90 | 0.84 | 0.76 | 0.70 | 0.63 | 0.54 | 0.44 | 0.39 | 0.35 | 0.31 | 0.27 | 0.25 |
|
| ||
1Crl8Ni9Ti | 0.98 | 0.93 | 0.88 | 0.83 | 0.78 | 0.75 | 0.72 | 0.69 | 0.66 | 0.65 | 0.63 | 0.61 | 0.59 | 0.57 | 0.55 | 0.53 | ||
ZG1Cr18Ni9Ti | 0.98 | 0.93 | 0.88 | 0.83 | 0.78 | 0.75 | 0.72 | 0.69 | 0.66 | 0.65 | 0.63 | 0.61 | 0.59 | 0.57 | 0.55 | 0.53 | ||
注1:温度或压力值处在所示值的中间时,可用内插法来求取最高使用压力或温度值。 | ||||||||||||||||||
注2:表中所指压力均为表压。 |