通用阀门 不绣钢铸件技术条件、铸件化学成分
| 牌号 | 化学成分%（除给出范围外的为最大值) | 引用标准 | ||||||||||
| C | Si | Mn | Cr | Ni | Mo | Cu | Ti | S | P | N | ||
| ZG03Cr18Ni10 | ≤0.03 | ≤1.5 | 0.8～2.0 | 17.0～20.0 | 8.0～12.0 | — | — | — | ≤0.030 | ≤0.040 | — | GB/T2100 GB/T5613
|
| ZG08Cr18Ni9 | ≤0.08 | 8.0～11.0 | — | — | — | — | ||||||
| ZG12Cr18Ni9 | ≤0.12 | — | — | — | ≤0.045 | — | ||||||
| ZG08Cr18Ni9Ti | ≤0.08 | — | — | 5(C-0.02) ～0.7 | ≤0.040 | — | ||||||
| ZG12Cr18Ni9Ti | ≤0.12 | — | — | ≤0.045 | — | |||||||
| ZG08Cr18Ni12Mo2Ti | ≤0.08 | 16.0～19.0 | 11.0～13.0 | 2.0～3.0 | — | ≤0.040 | — | |||||
| ZG12Cr18Ni12Mo2Ti | ≤0.12 | — | ≤0.045 | — | ||||||||
| ZG12Cr17Mn9Ni4Mo3Cu2N | 8.0～10.0 | 3.0～5.0 | 2.9～3.5 | 2.0～2.5 | — | ≤0.035 | ≤0.060 | 0.16～0.26 | ||||
| ZG12Cr18Mn13Mo2CuN | 12.0～14.0 | 17.0～20.0 | — | 1.5～2.0 | 1.0～1.5 | — | 0.19～0.26 | |||||
| CF3 | 0.03 | 2.00 | 1.5 | 17.0～21.0 | 8.0～12.0 | 0.50 | — | — | 0.04 | 0.04 | — | ASTM A351/ A351M: 2000 |
| CF8 | 0.08 | 18.0～21.0 | 8.0～11.0 | 0.50 | — | — | — | |||||
| CF3M | 0.03 | 1.5 | 17.0～21.0 | 9.0～13.0 | 2.0～3.0 | — | — | — | ||||
| CF8M | 0.08 | 18.0～21.0 | 9.0～12.0 | — | — | — | ||||||
| CF8C | 2.00 | 0.50 | — | — | — | |||||||